Clarification of a wheat straw‐derived medium with ion‐exchange resins for xylitol crystallization

BACKGROUND: Xylitol bioproduction from lignocellulosic residues comprises hydrolysis of the hemicellulose, detoxification of the hydrolysate, bioconversion of the xylose, and recovery of xylitol from the fermented hydrolysate. There are relatively few reports on xylitol recovery from fermented media. In the present study, ion‐exchange resins were used to clarify a fermented wheat straw hemicellulosic hydrolysate, which was then vacuum‐concentrated and submitted to cooling in the presence of ethanol for xylitol crystallization. RESULTS: Sequential adsorption into two anion‐exchange resins (A‐860S and A‐500PS) promoted considerable reductions in the content of soluble by‐products (up to 97.5%) and in medium coloration (99.5%). Vacuum concentration led to a dark‐colored viscous solution that inhibited xylitol crystallization. This inhibition could be overcome by mixing the concentrated medium with a commercial xylitol solution. Such a strategy led to xylitol crystals with up to 95.9% purity. The crystallization yield (43.5%) was close to that observed when using commercial xylitol solution (51.4%). CONCLUSION: The experimental data demonstrate the feasibility of using ion‐exchange resins followed by cooling in the presence of ethanol as a strategy to promote the fast recovery and purification of xylitol from hemicellulose‐derived fermentation media. Copyright © 2008 Society of Chemical Industry     

The effect of CaF<Subscript>2</Subscript> on thermodynamics of CaO-CaF<Subscript>2</Subscript>-SiO<Subscript>2</Subscript>(-MgO) slags

To address the role of CaF₂ in the CaO-CaF₂-SiO₂(-MgO) slag system employed for the production of low-pressure rotor steels, the thermodynamic aspects of the slag were investigated by equilibrating it with liquid iron at 1873 K in CaO or MgO crucibles. Presaturation of slag with an oxide block piece of CaO or MgO in a Pt crucible and application of a carbon paste to the outside of an oxide crucible were designed to prevent crucible failure during the slag-metal experiments. The liquidus isotherm and phase boundary of the preceding slag system were investigated using the slag-metal equilibria. Also, the effect of CaF₂ on the sulfide capacity and the activity coefficient of Fe _t O were of particular interest in controlling the sulfur level and cleanliness of low-pressure rotor steels.     

Transmission Fiber Chromatic Dispersion Dependence on Temperature: Implications on 40 Gb/s Performance

In this letter, we will evaluate the performance degradation of a 40 km high‐speed (40 Gb/s) optical system, induced by optical fiber variations of the chromatic dispersion induced by temperature changes. The chromatic dispersion temperature sensitivity will be estimated based on the signal quality parameters.     

Enhancement mode InP MISFET's with sulfide passivation andphoto-CVD grown P3N5 gate insulators

High performance enhancement mode InP MISFET's have been successfully fabricated by using the sulfide passivation for lower interface states and with photo-CVD grown P₃N₅ film used as gate insulator. The MISFET's thus fabricated exhibited exhibited pinch-off behavior with essentially no hysteresis. Furthermore the device showed a superior stability of drain current. Specifically under the gate bias of 2 V for 10⁴ seconds the room temperature drain current was shown to reduce from the initial value merely by 2.9% at the drain voltage of 4 V. The effective electron mobility and extrinsic transconductance are found to be about 2300 cm ²/V·s and 2.7 mS/mm, respectively. The capacitance-voltage characteristics of the sulfide passivated InP MIS diodes show little hysteresis and the minimum density of interface trap states as low as 2.6×10¹⁴/cm² eV has been attained     

Pressure effects on flow and fracture of Be-Al alloys

The flow and fracture behavior of Be-Al alloys were determined in tension with different levels of superimposed pressure. The Be-Al alloys were prepared by Brush Wellman, Inc. (Cleveland, OH) from prealloyed powders processed to either a hot isostatically pressed (“hipped”) or cold isostatically pressed and extruded condition. Significant effects of pressure on both the flow and ductility have been observed at room temperature, with implications on the formability of these materials. The effects of changes in processing conditions and stress state on the flow and fracture behavior are summarized in addition to both optical and scanning electron microscopy (SEM) examination of the fracture surfaces. Separate other studies on the alloy constituents (e.g., Al and Be) are also reported. The results are also compared to previous works on monolithic materials and composites tested with high pressure.